In order to find out the influence of sintering additives on the electrical conductivity of Si₃N₄-based ceramics composites with dispersed carbon nano-fibers (CNFs) two different mixtures of sintering additives were tested – Al₂O₃/Yb₂O₃ and MgSiN₂/Yb₂O₃, respectively. Optimization of hot-pressing conditions was performed for each mixture. The results show that the electrical conductivity can be effectively increased up to 1315 S/m by replacement of traditional sintering aid – alumina, with magnesium silicon nitride, while the mechanical properties remained on the same level. Other advantages of using MgSiN₂ instead of alumina are the preservation of higher amounts of CNFs in the ceramic composite and lower densification temperature (1500 °C) compared to samples sintered with alumina-based sintering aids (1550 °C).